Rheological properties |
C |
Melt volume-flow rate |
270 °C; 5 kg |
cm³/(10 min) |
ISO 1133-1 |
50 |
C |
Molding shrinkage, parallel |
60x60x2; 250 °C / WZ 80° C; 600 bar |
% |
ISO 294-4 |
1.8 |
C |
Molding shrinkage, transverse |
60x60x2; 250 °C / WZ 80° C; 600 bar |
% |
ISO 294-4 |
1.8 |
|
Post- shrinkage, parallel |
60x60x2; 120 °C; 4 h |
% |
ISO 294-4 |
0.4 |
|
Post- shrinkage, transverse |
60x60x2; 120 °C; 4 h |
% |
ISO 294-4 |
0.4 |
Mechanical properties (23 °C/50 % r. h.) |
C |
Tensile modulus |
1 mm/min |
MPa |
ISO 527-1,-2 |
2300 |
C |
Yield stress |
50 mm/min |
MPa |
ISO 527-1,-2 |
45 |
C |
Yield strain |
50 mm/min |
% |
ISO 527-1,-2 |
4.5 |
C |
Nominal strain at break |
50 mm/min |
% |
ISO 527-1,-2 |
>15 |
C |
Tensile creep modulus |
1 h |
MPa |
ISO 899-1 |
2300 |
C |
Tensile creep modulus |
1000 h |
MPa |
ISO 899-1 |
1600 |
C |
Charpy impact strength |
23 °C |
kJ/m² |
ISO 179-1eU |
N |
C |
Charpy impact strength |
-30 °C |
kJ/m² |
ISO 179-1eU |
105 |
C |
Charpy notched impact strength |
23 °C |
kJ/m² |
ISO 179-1eA |
< 10 |
C |
Charpy notched impact strength |
-30 °C |
kJ/m² |
ISO 179-1eA |
< 10 |
|
Izod impact strength |
23 °C |
kJ/m² |
ISO 180-1U |
N |
|
Izod impact strength |
-30 °C |
kJ/m² |
ISO 180-1U |
65 |
|
Izod notched impact strength |
23 °C |
kJ/m² |
ISO 180-1A |
< 10 |
|
Izod notched impact strength |
-30 °C |
kJ/m² |
ISO 180-1A |
< 10 |
|
Izod notched impact strength |
-40 °C |
kJ/m² |
ISO 180-1A |
< 10 |
|
Flexural modulus |
2 mm/min |
MPa |
ISO 178-A |
2300 |
|
Flexural strength |
2 mm/min |
MPa |
ISO 178-A |
75 |
|
Flexural strain at flexural strength |
2 mm/min |
% |
ISO 178-A |
5.3 |
|
Flexural stress at 3.5 % strain |
2 mm/min |
MPa |
ISO 178-A |
70 |
|
Energy to peak force |
23 °C |
Nm |
acc. ISO 6603-2 |
80 |
|
Ball indentation hardness |
|
N/mm² |
ISO 2039-1 |
120 |
Thermal properties |
C |
Melting temperature |
10 °C/min |
°C |
ISO 11357-1,-3 |
225 |
C |
Temperature of deflection under load |
1.80 MPa |
°C |
ISO 75-1,-2 |
65 |
C |
Temperature of deflection under load |
0.45 MPa |
°C |
ISO 75-1,-2 |
125 |
|
Vicat softening temperature |
50 N; 120 °C/h |
°C |
ISO 306 |
150 |
C |
Coefficient of linear thermal expansion, parallel |
23 to 55 °C |
10-4/K |
ISO 11359-1,-2 |
1.1 |
C |
线性热膨胀系数,遇到横向e |
23 to 55 °C |
10-4/K |
ISO 11359-1,-2 |
1.1 |
C |
Burning behavior UL 94 |
1.5 mm |
Class |
UL 94 |
V-0 |
C |
Burning behavior UL 94 |
0.75 mm |
Class |
UL 94 |
V-2 |
C |
Oxygen index |
Method A |
% |
ISO 4589-2 |
30 |
|
Thermal conductivity |
23 °C |
W/(m·K) |
ISO 8302 |
0.25 |
|
Resistance to heat (ball pressure test) |
|
°C |
IEC 60695-10-2 |
190 |
|
Temperature index (Tensile strength) |
20000 h |
°C |
IEC 60216-1 |
135 |
|
Halving interval (Tensile strength) |
|
°C |
IEC 60216-1 |
5.8 |
|
Relative temperature index (Tensile strength) |
|
°C |
UL 746B |
125 |
|
Temperature index (Tensile impact strength) |
20000 h |
°C |
IEC 60216-1 |
120 |
|
Halving interval (Tensile impact strength) |
|
°C |
IEC 60216-1 |
5.3 |
|
Relative temperature index (Tensile impact strength) |
|
°C |
UL 746B |
115 |
|
Temperature index (Electric strength) |
20000 h |
°C |
IEC 60216-1 |
135 |
|
Halving interval (Electric strength) |
|
°C |
IEC 60216-1 |
5.8 |
|
Relative temperature index (Electric strength) |
|
°C |
UL 746B |
125 |
|
Glow wire test (GWFI) |
0.75 mm |
°C |
IEC 60695-2-12 |
960 |
Electrical properties (23 °C/50 % r. h.) |
C |
Relative permittivity |
100 Hz |
- |
IEC 60250 |
3.8 |
C |
Relative permittivity |
1 MHz |
- |
IEC 60250 |
3.6 |
C |
Dissipation factor |
100 Hz |
10-4 |
IEC 60250 |
40 |
C |
Dissipation factor |
1 MHz |
10-4 |
IEC 60250 |
240 |
C |
Volume resistivity |
|
Ohm·m |
IEC 60093 |
>1E15 |
C |
Surface resistivity |
|
Ohm |
IEC 60093 |
>1E15 |
C |
Electric strength |
1 mm |
kV/mm |
IEC 60243-1 |
23 |
C |
Comparative tracking index CTI |
Solution A |
Rating |
IEC 60112 |
600 |
Other properties (23 °C) |
C |
Water absorption (Saturation value) |
Water at 23 °C |
% |
ISO 62 |
0.6 |
C |
Water absorption (Equilibrium value) |
23 °C; 50 % RH |
% |
ISO 62 |
0.2 |
C |
Density |
|
kg/m³ |
ISO 1183 |
1380 |
|
Bulk density |
|
kg/m³ |
ISO 60 |
800 |
Processing conditions for test specimens |
C |
Injection molding-Melt temperature |
|
°C |
ISO 294 |
250 |
C |
Injection molding-Mold temperature |
|
°C |
ISO 294 |
80 |
Processing recommendations |
|
Drying temperature circulating air dryer |
|
°C |
- |
120 |
|
Drying time circulating air dryer |
|
h |
- |
4-8 |
|
Residual moisture content |
|
% |
Acc. to Karl Fischer |
0-0.02 |
|
Melt temperature (Tmin - Tmax) |
|
°C |
- |
240-260 |
|
Mold temperature |
|
°C |
- |
80-100 |