| Rheological properties |
| C |
Molding shrinkage, parallel |
60x60x2; 280 °C / MT 80 °C; 500 bar |
% |
ISO 294-4 |
0.4 |
|
| C |
Molding shrinkage, transverse |
60x60x2; 280 °C / MT 80 °C; 500 bar |
% |
ISO 294-4 |
0.5 |
|
|
Post- shrinkage, parallel |
60x60x2; 120 °C; 4 h |
% |
ISO 294-4 |
0.1 |
|
|
Post- shrinkage, transverse |
60x60x2; 120 °C; 4 h |
% |
ISO 294-4 |
0.1 |
|
Mechanical properties (23 °C/50 % r. h.) |
| C |
Tensile modulus |
1毫米/min |
MPa |
ISO 527-1,-2 |
12100 |
6000 |
| C |
Tensile Stress at break |
5 mm/min |
MPa |
ISO 527-1,-2 |
120 |
73 |
| C |
Tensile Strain at break |
5 mm/min |
% |
ISO 527-1,-2 |
1.6 |
2.2 |
| C |
Charpy impact strength |
23 °C |
kJ/m² |
ISO 179-1eU |
30 |
23 |
|
伊佐德冲击强度 |
23 °C |
kJ/m² |
ISO 180-1U |
25 |
22 |
|
Izod notched impact strength |
23 °C |
kJ/m² |
ISO 180-1A |
<10 |
<10 |
|
Flexural modulus |
2 mm/min |
MPa |
ISO 178-A |
12300 |
6000 |
|
Flexural strength |
2 mm/min |
MPa |
ISO 178-A |
175 |
110 |
|
Flexural strain at flexural strength |
2 mm/min |
% |
ISO 178-A |
1.8 |
2.6 |
热性能 |
| C |
Melting temperature |
10 °C/min |
°C |
ISO 11357-1,-3 |
220 |
|
| C |
Temperature of deflection under load |
1.80兆帕 |
°C |
ISO 75-1,-2 |
181 |
|
| C |
Temperature of deflection under load |
0.45 MPa |
°C |
ISO 75-1,-2 |
200 |
|
|
Vicat softening temperature |
50 N; 120 °C/h |
°C |
ISO 306 |
204 |
|
| C |
Coefficient of linear thermal expansion, parallel |
23 to 55 °C |
10-4/K |
ISO 11359-1,-2 |
0.3 |
|
| C |
线性热膨胀系数,transverse |
23 to 55 °C |
10-4/K |
ISO 11359-1,-2 |
0.5 |
|
|
Thermal conductivity, in-plane |
|
W/(m·K) |
ISO 22007-4 |
1.1 |
|
|
Thermal conductivity, through-plane |
|
W/(m·K) |
ISO 22007-4 |
0.9 |
|
| C |
Burning behavior UL 94 |
1.5 mm |
Class |
UL 94 |
V-0 |
|
|
Burning behavior UL 94 |
1.2 mm |
Class |
UL 94 |
V-0 |
|
| C |
Oxygen index |
Method A |
% |
ISO 4589-2 |
49.1 |
|
|
Glow wire test (GWFI) |
0.8 mm |
°C |
IEC 60695-2-12 |
960 |
|
|
Glow wire test (GWIT) |
0.8 mm |
°C |
IEC 60695-2-13 |
775 |
|
Electrical properties (23 °C/50 % r. h.) |
| C |
Electric strength |
1毫米 |
kV/mm |
IEC 60243-1 |
26.3 |
|
| C |
Comparative tracking index CTI |
Solution A |
Rating |
IEC 60112 |
600 |
|
其他性能（23°C） |
| C |
Density |
|
kg/m³ |
ISO 1183 |
1690 |
|
Processing conditions for test specimens |
| C |
Injection molding-Melt temperature |
|
°C |
ISO 294 |
260 |
|
| C |
Injection molding-Mold temperature |
|
°C |
ISO 294 |
80 |
|
Processing recommendations |
|
Drying temperature dry air dryer |
|
°C |
- |
80 |
|
|
Drying time dry air dryer |
|
h |
- |
2-6 |
|
|
Residual moisture content |
|
% |
Acc. to Karl Fischer |
0.03-0.07 |
|
|
Melt temperature (Tmin - Tmax) |
|
°C |
- |
250-280 |
|
|
Mold temperature |
|
°C |
- |
80-100 |
|
|
| This information and our technical advice - whether verbal, in writing or by way of trials - are given in good faith but without warranty, and this also applies where proprietary rights of third parties are involved. Our advice does not release you from the obligation to verify the information currently provided - especially that contained in our safety data and technical information sheets - and to test our products as to their suitability for the intended processes and uses. The application, use and processing of our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore, entirely your own responsibility. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery. |
| Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as guide values only and not as binding minimum values. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the coloring. |
| 在推荐的加工条件下，加工过程中可能会放出少量的分解产物。为避免对机器操作人员的健康和福利造成任何风险，必须根据安全数据表，通过在工作场所提供有效的排气通风和新鲜空气来确保工作环境的公差限制。为了防止聚合物的部分分解和挥发性分解产物的产生，不应超过规定的加工温度。由于过高的温度通常是由于操作员的错误或加热系统的缺陷造成的，因此在这些区域必须特别小心和控制。 |
| Conditioning in accordance with ISO 1110 (70 °C; 62 % r.h.) |