Durethan BKV35H3.0 000000
_More Info
_Data sheet ISO (PDF)

Data sheet
PA 6, 35 % glass fibers, injection molding, heat-aging stabilized
ISO Shortname:ISO16396-PA 6, GF35, GHR, S14-110
Property Test Condition Unit Standard guide value
d.a.m。 cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.23
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.68
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.05
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.07

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1毫米/min MPa ISO 527-1,-2 11000 6800
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 190 120
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 5.0
C Tensile creep modulus 1 h MPa ISO 899-1 6000
C Tensile creep modulus 1000 h MPa ISO 899-1 4900
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 85 95
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 75 75
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 15 22
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 10 10
Izod冲击力量 23 °C kJ/m² ISO 180-1U 80 90
Izod冲击力量 -30 °C kJ/m² ISO 180-1U 70 65
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 15 22
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 10 10
Flexural modulus 2 mm/min MPa ISO 178-A 10700 5900
Flexural strength 2 mm/min MPa ISO 178-A 290 180
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.0 5.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 160

热性能
C Melting temperature 10 °C/min °C ISO 11357-1,-3 222.
C Temperature of deflection under load 1.80 MPa. °C ISO 75-1,-2 205
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 215
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 > 200
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.2
C 线性热膨胀系数,transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.8
C Burning behavior UL 94 1.5 mm Class UL 94 HB
Glow wire test (GWFI) 2.0 mm °C IEC 60695-2-12 650
燃烧行为US-FMVSS302 ISO 3795. passed

Electrical properties (23 °C/50 % r. h.)
C Relative permittivity 100 Hz - IEC 60250 4.0 15
C Relative permittivity 1 MHz - IEC 60250 4.0 5.0
C Dissipation factor 100 Hz 10-4 IEC 60250 70 2000
C Dissipation factor 1 MHz 10-4 IEC 60250 150 1200.
C Volume resistivity Ohm·m IEC 60093 1E13 1E10
C Surface resistivity Ohm IEC 60093 1E14 1E12
C Electric strength 1毫米 kV/mm IEC 60243-1 40 35
C Comparative tracking index CTI Solution A Rating IEC 60112 525

其他性质（23°C）
C Water absorption (Saturation value) Water at 23 °C % ISO 62 6.5
C Water absorption (Equilibrium value) 23 °C; 50 % RH % ISO 62 1.9
C Density kg/m³ ISO 1183 1410

Processing conditions for test specimens
C Injection molding-Melt temperature °C ISO 294 280
C Injection molding-Mold temperature °C ISO 294 80

Processing recommendations
Drying temperature dry air dryer °C - 80
Drying time dry air dryer h - 2-6
Residual moisture content % Acc. to Karl Fischer 0.03-0.12
Melt temperature (Tmin - Tmax) °C - 270-290
Mold temperature °C - 80-120
C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Disclaimer
Disclaimer for commercial products
This information and our technical advice - whether verbal, in writing or by way of trials - are given in good faith but without warranty, and this also applies where proprietary rights of third parties are involved. Our advice does not release you from the obligation to verify the information currently provided - especially that contained in our safety data and technical information sheets - and to test our products as to their suitability for the intended processes and uses. The application, use and processing of our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore, entirely your own responsibility. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.
Test values
Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as guide values only and not as binding minimum values. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the coloring.
Processing note
在推荐的加工条件下，可以在处理期间缩小量的分解产物。为了妨碍机器操作性的健康和福祉的任何风险，必须根据安全数据表提供工作场所的高效排气通风和新鲜空气来确保工作环境的公差限制。为了防止聚合物的部分分解和挥发性分解产物的产生，不应大大超过规定的加工温度。由于过高的温度通常是运营商误差或加热系统中的缺陷的结果，因此在这些区域中的特殊护理和控制是必不可少的。
Conditioning
Conditioning in accordance with ISO 1110 (70 °C; 62 % r.h.)