Rheological properties |
C |
Melt volume-flow rate |
250 °C; 2.16 kg |
cm³/(10 min) |
ISO 1133-1 |
55 |
C |
Molding shrinkage, parallel |
60x60x2; 250 °C / WZ 80° C; 600 bar |
% |
ISO 294-4 |
2.3 |
C |
Molding shrinkage, transverse |
60x60x2; 250 °C / WZ 80° C; 600 bar |
% |
ISO 294-4 |
2.3 |
|
Post- shrinkage, parallel |
60x60x2; 120 °C; 4 h |
% |
ISO 294-4 |
0.2 |
|
Post- shrinkage, transverse |
60x60x2; 120 °C; 4 h |
% |
ISO 294-4 |
0.1 |
Mechanical properties (23 °C/50 % r. h.) |
C |
Tensile modulus |
1毫米/min |
MPa |
ISO 527-1,-2 |
2300 |
C |
Yield stress |
50 mm/min |
MPa |
ISO 527-1,-2 |
55 |
C |
Yield strain |
50 mm/min |
% |
ISO 527-1,-2 |
8.0 |
C |
Nominal strain at break |
50 mm/min |
% |
ISO 527-1,-2 |
10 |
C |
Charpy impact strength |
23 °C |
kJ/m² |
ISO 179-1eU |
75 |
|
Izod冲击力量 |
23 °C |
kJ/m² |
ISO 180-1U |
65 |
|
Izod notched impact strength |
23 °C |
kJ/m² |
ISO 180-1A |
<10 |
|
Flexural modulus |
2 mm/min |
MPa |
ISO 178-A |
2100 |
|
Flexural strength |
2 mm/min |
MPa |
ISO 178-A |
75 |
|
Flexural strain at flexural strength |
2 mm/min |
% |
ISO 178-A |
6.5 |
|
Flexural stress at 3.5 % strain |
2 mm/min |
MPa |
ISO 178-A |
60 |
|
Ball indentation hardness |
|
N/mm² |
ISO 2039-1 |
120 |
热性能 |
C |
Melting temperature |
10 °C/min |
°C |
ISO 11357-1,-3 |
224. |
C |
Temperature of deflection under load |
1.80 MPa. |
°C |
ISO 75-1,-2 |
75 |
C |
Temperature of deflection under load |
0.45 MPa |
°C |
ISO 75-1,-2 |
160 |
|
Vicat softening temperature |
50 N; 120 °C/h |
°C |
ISO 306 |
185 |
C |
Coefficient of linear thermal expansion, parallel |
23 to 55 °C |
10-4/K |
ISO 11359-1,-2 |
1.2 |
C |
Coefficient of linear thermal expansion, transverse |
23 to 55 °C |
10-4/K |
ISO 11359-1,-2 |
1.2 |
C |
Burning behavior UL 94 |
1.5 mm |
Class |
UL 94 |
V-2 |
C |
Burning behavior UL 94 |
0.75 mm |
Class |
UL 94 |
V-2 |
C |
Oxygen index |
Method A |
% |
ISO 4589-2 |
28 |
|
Resistance to heat (ball pressure test) |
|
°C |
IEC 60695-10-2 |
202 |
|
Glow wire test (GWFI) |
0.4 mm |
°C |
IEC 60695-2-12 |
960 |
|
Glow wire test (GWFI) |
0.75 mm |
°C |
IEC 60695-2-12 |
960 |
|
Glow wire test (GWFI) |
1.5 mm |
°C |
IEC 60695-2-12 |
960 |
|
Glow wire test (GWIT) |
0.75 mm |
°C |
IEC 60695-2-13 |
800 |
|
Glow wire test (GWIT) |
1.5 mm |
°C |
IEC 60695-2-13 |
800 |
|
Glow wire test (GWIT) |
3.0 mm |
°C |
IEC 60695-2-13 |
800 |
Electrical properties (23 °C/50 % r. h.) |
C |
Volume resistivity |
|
Ohm·m |
IEC 60093 |
>1E13 |
C |
Surface resistivity |
|
Ohm |
IEC 60093 |
>1E15 |
C |
Electric strength |
1毫米 |
kV/mm |
IEC 60243-1 |
30 |
C |
Comparative tracking index CTI |
Solution A |
Rating |
IEC 60112 |
600 |
|
Comparative tracking index CTI |
Solution A |
PLC |
UL 746A |
0 |
其他性质(23°C) |
C |
Density |
|
kg/m³ |
ISO 1183 |
1320. |
|
Bulk density |
|
kg/m³ |
ISO 60 |
800 |
Processing conditions for test specimens |
C |
Injection molding-Melt temperature |
|
°C |
ISO 294 |
250 |
C |
Injection molding-Mold temperature |
|
°C |
ISO 294 |
80 |
Processing recommendations |
|
Drying temperature circulating air dryer |
|
°C |
- |
120 |
|
Drying time circulating air dryer |
|
h |
- |
4-8 |
|
Residual moisture content |
|
% |
Acc. to Karl Fischer |
0-0.02 |
|
Melt temperature (Tmin - Tmax) |
|
°C |
- |
240-260 |
|
Tmax的可接受停留时间 |
|
min |
- |
<5 |
|
Mold temperature |
|
°C |
- |
80-100 |
|
This information and our technical advice - whether verbal, in writing or by way of trials - are given in good faith but without warranty, and this also applies where proprietary rights of third parties are involved. Our advice does not release you from the obligation to verify the information currently provided - especially that contained in our safety data and technical information sheets - and to test our products as to their suitability for the intended processes and uses. The application, use and processing of our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore, entirely your own responsibility. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery. |
Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as guide values only and not as binding minimum values. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the coloring. |